Photoinduced oxygen release and persistent photoconductivity in ZnO nanowires
View/ Open
Author
Bao, Jiming
Shalish, Ilan
Su, Zhihua
Gurwitz, Ron
Capasso, Federico
Wang, Xiaowei
Ren, Zhifeng
Published Version
https://doi.org/10.1186/1556-276X-6-404Metadata
Show full item recordCitation
Bao, Jiming, Ilan Shalish, Zhihua Su, Ron Gurwitz, Federico Capasso, Xiaowei Wang, and Zhifeng Ren. 2011. “Photoinduced Oxygen Release and Persistent Photoconductivity in ZnO Nanowires.” Nanoscale Research Letters 6 (1): 404. https://doi.org/10.1186/1556-276x-6-404.Abstract
Photoconductivity is studied in individual ZnO nanowires. Under ultraviolet (UV) illumination, the induced photocurrents are observed to persist both in air and in vacuum. Their dependence on UV intensity in air is explained by means of photoinduced surface depletion depth decrease caused by oxygen desorption induced by photogenerated holes. The observed photoresponse is much greater in vacuum and proceeds beyond the air photoresponse at a much slower rate of increase. After reaching a maximum, it typically persists indefinitely, as long as good vacuum is maintained. Once vacuum is broken and air is let in, the photocurrent quickly decays down to the typical air-photoresponse values. The extra photoconductivity in vacuum is explained by desorption of adsorbed surface oxygen which is readily pumped out, followed by a further slower desorption of lattice oxygen, resulting in a Zn-rich surface of increased conductivity. The adsorption-desorption balance is fully recovered after the ZnO surface is exposed to air, which suggests that under UV illumination, the ZnO surface is actively "breathing" oxygen, a process that is further enhanced in nanowires by their high surface to volume ratio.Terms of Use
This article is made available under the terms and conditions applicable to Other Posted Material, as set forth at http://nrs.harvard.edu/urn-3:HUL.InstRepos:dash.current.terms-of-use#LAACitable link to this page
http://nrs.harvard.edu/urn-3:HUL.InstRepos:41371563
Collections
- FAS Scholarly Articles [18176]
Contact administrator regarding this item (to report mistakes or request changes)