SnS is a promising earth-abundant material for photovoltaic applications. Heterojuction solar cells were made by vapor deposition of p-type tin(II) sulfide, SnS, and n-type zinc oxysulfide, Zn(O,S), using a device structure of soda-lime glass/Mo/SnS/Zn(O,S)/ZnO/ITO. A record efficiency was achieved for SnS-based thin-film solar cells by varying the oxygen-to-sulfur ratio in Zn(O,S). Increasing the sulfur content in Zn(O,S) raises the conduction band offset between Zn(O,S) and SnS to an optimum slightly positive value. A record SnS/Zn(O,S) solar cell with a S/Zn ratio of 0.37 exhibits short circuit current density ((J_{sc})), open circuit voltage ((V_{oc})), and fill factor (FF) of (19.4 mA/cm^{2}), 0.244 V, and 42.97%, respectively, as well as an NREL-certified total-area power-conversion efficiency of 2.04% and an uncertified active-area efficiency of 2.46%.

Zinc oxysulfide, Zn(O,S), films grown by atomic layer deposition were annealed in oxygen to adjust the carrier concentration. The electron carrier concentration of Zn(O,S) can be reduced by several orders of magnitude from (10^{19}) to (10^{15} cm^{−3}) by post-deposition annealing in oxygen at temperatures from 200 °C to 290 °C. In the case of Zn(O,S) with S/Zn = 0.37, despite the considerable change in the electron carrier concentration, the bandgap energy decreased by only ∼0.1 eV, and the crystallinity did not change much after annealing. The oxygen/zinc ratio increased by 0.05 after annealing, but the stoichiometry remained uniform throughout the film.